Carboni microporosi da nanospugne di oligosaccaridi: sintesi, caratterizzazione e controllo della morfologia.

The following thesis work aims at obtaining single-step monolithic microporous carbons having a surface area of at least 500 m2 / g and with good mechanical properties. For the production of porous coal, the precursor will undergo a pyrolysis thermal treatment. The tests will be conducted in parallel on two separate carbon precursors. The investigated carbon precursors will be two nanosponges, one produced by cross-linking β-cyclodextrin with pyromellitic dianhydride in a 1: 4 molar ratio and the second one also produced by a cross-linking reaction between a polysaccharide (Line Caps) and pyromellitic dianhydride always in ratio 1 4. Moreover, in this Thesis work, the influence of the nanospong granulometry on the surface area and on the morphology of the produced carbon was studied.

Il seguente lavoro di tesi ha come scopo l'ottenimento di carboni microporosi monolitici single-step aventi area superficiale di almeno 500 m2/g e con buone proprietà meccaniche. Per la produzione del carbone poroso il precursore subirà un trattamento termico di pirolisi. Le prove verranno condotte in parallelo su due distinti precursori di carbonio. I precursori di carbonio indagati saranno due nanospugne, una prodotta reticolando β-ciclodestrine con dianidride piromellitica in rapporto 1:4 molare e la seconda prodotta anch'essa da una reazione di reticolazione fra un polisaccaride (Line Caps) e dianidride piromellitica sempre in rapporto 1:4. Inoltre, in questo lavoro di Tesi, è stata studiata l'influenza della granulometria della nanospugne sull'area superficiale e sulla morfologia del carbone prodotto.