Caratterizzazione di saldature laser di giunti rame-alluminio

Laser welding of copper-aluminum joints represents an important application in the automotive and electronics industries. However, there are several problems: as can be seen from the phase diagram, the two metals tend to form numerous intermetallic compounds, whose covalent nature makes them fragile materials with low electrical conductivity. The aim of the work was to optimize (in collaboration with FST of Pinerolo), through metallographic and electrochemical characterizations, the process parameters of the laser welders with the aim of obtaining resistant welds, with the highest possible conductivity and with the absence of defects.

Le saldature laser di giunti rame-alluminio rappresentano un applicazione importante per quanto riguarda l'industria dell'automotive e dell'elettronica. Tuttavia ci sono diverse problematiche: come si può notare dal diagramma di fase, i due metalli tendono a formare numerosi composti intermetallici, la cui natura covalente li rende materiali fragili e con bassa conducibilità elettrica. Lo scopo del lavoro è stato quello di ottimizzare (in collaborazione con FST di Pinerolo), attraverso caratterizzazioni metallografiche ed elettrochimiche, i parametri di processo delle saldatrici laser con in il fine di ottenere saldature resistenti, con la più alta conducibilità possibile e con assenza di difetti.